| High Hardness MS Hybrid Sealant HM-MS810X |
| Items |
C*a/T*b/S*c/O*d |
Unit |
Typical Value |
Requirement |
Test Std. |
Eqv. Std. |
| Appearance |
|
- |
White,Black,Gray,Red,Blue......
|
Fine, uniform paste without bubbles, crusts, gels |
Test StQ/QY-00-T001d |
- |
| Density |
|
g/cm3 |
1.08 |
1.1±0.05 |
GB/T 13477.2 |
- |
| Tack free |
Properties Uncured |
min |
20 |
≤30 |
GB/T 13477.5 |
ASTM D2377:2000 |
| Hardness, Shore A |
Properties Cured |
- |
70 |
≥70 |
GB/T 531.1 |
ISO 7619-1:2004 |
| Elongation at break |
Properties Cured |
% |
- |
- |
GB/T 528 |
ISO 37:2005 |
| Tensile Strength |
Properties Cured |
MPa |
- |
- |
GB/T 528 |
ISO 37:2005 |
These figures are only intended as a guide and should not be used in preparing specifications.
PRODUCT DESCRIPTION
MS810X is a series high hardness MS hybrid polymer sealant. it is made of Howell own technology MS polymer and shows a good performance to applications that require high hardness and high strength. It offers different colors choice, solvent free, low VOC and paintable, thus an ideal sealant for bonding parts need high hardness such as anti-mold, nai free etc.
- Fully transparent
- Strong bonding on almost all surfaces
-
- One component, easy to process
- Eco friendly-no isocyanate, solvent, halogen or acid components: harmless to health-
- Paintable with water based coatings
APPLICATIONS
Sealing the construction or structures requiring high hardness
Sanitary and kitchen application: Nail-free, waterproof and anti-mold applications
USAGE
Construction:
Cut the branch opening, put on the glue nozzle, cut the glue nozzle into a suitable slope, and apply it tothe construction site with a glue extrusion gun. During pneumatic gluing, the air pressure isrecommended not to exceed 0.4 MPa, and the construction temperature is recommended to be 4°C -40°C
Curing:
Place the glued parts in the air. After the skin is formed, it will cure from the surface to the inside. Thecuring depth will be 2~4mm within 24 hours at room temperature and 55% relative humidity. As timegoes by, the curing depth gradually increases.
Storage:
Unused glue should be tightened immediately and the nozzle should be sealed for storage. When usingit again, if there is a little crust on the seal, just remove it and it will not affect normal use. During thestorage process, a small amount of crusting may also appear on the branch mouth. After removal, it canbe used normally without affecting product performance.
PACKAGE
Standard 300ml plastic bottle packing, 24pcs/carton; 500-600ml flexible film packing, 20pcs/carton;A variety of packaging options are available to meet your needs.
Store the original sealant in a dry place, the temperature should not be higher than 27 °C, and the storageperiod is 12 months from the date of production
SAFETY PRECAUTIONS
Ensure the product is kept out of children's reach. Always read the product specifications, material details, and instructions on the container packaging before use.
Company Profile
Nanjing Howell New Materials Technology Co., Ltd.
Room 501, Unit 7, Xingzhihui, Xinghuo Rd 19th, Jiangbei New District, Nanjing, (211899), Jiangsu, China.
American Warehouse:Add: 1006 CROCKER RD, DOOR E5, WESTLAKE, OH 44145
Audited Supplier 
){kind=link}