WR30 Weatherproofing building construction sealant and adhesive neutral cure oxime silicone

Product Description

 

1.Before curing

Property	Value	Test Method
Sagging(mm)	0	GB/T13477.5-2003
Surface drying time(h)	≤2	GB/T13477.5-2003
Depth curing rate	1-2mm/day	-
Complete curing time (humidity50±5%,temperature23±2ºC)	14-21 days	-

After curing for 21 days under conditions of humidity 50±5% ,temperature 23±2ºC

Property	Value	Test Method
Hardness (Shore A)	40	GB/T531-1999
Tensile modulus at 60% elongation (MPa)	No damage	GB/T13477.8-2003
Ultimate strength(MPa)	0.7	GB/T13477.8-2003
Ultimate elongation%	200	GB/T13477.8-2003
Sealant grade	12.5E	JC/T881-884-2001

*The above data are tested at 25ºC,50% relative humidity
*Standard colors white, black, gray

Product Description

HM-WR30 neutral silicone sealant is a one-component, neutral curing silicone sealant rubber that has good adhesion to various building materials without primer. 
 

Typical Applications

Sealing and caulking applications between various metal and aluminum alloy doors,windows and walls
Other general purpose caulking and waterproof sealing

USAGE

It cannot be used for structural assembly
Do not use on surfaces where plasticizers or solvents may leak out, as this may cause damage to the sealant
It is not recommended to use it in a completely sealed space, which will cause it to not be able to cure completely due to lack of moisture
It is not recommended to use it in places that have been immersed in water for a long time
It is not recommended for structural surfaces that will come into direct contact with food
It is not recommended to use it on medical devices.
 

CONSTRUCTION

1. Cleaning of substrate surface

(1) The purpose of surface treatment before bonding is to remove oil, dust, surface damage and loose natural oxide film on the surface of the base material during the production and transportation process, so as to roughen the surface of the base material and form a surface suitable for mechanism embedding. morphology, while improving surface chemical properties and improving durability under the influence of stress environmental factors.

(2) Cleaning solvents are usually isopropyl alcohol, methyl ethyl ketone, and xylene. The cleaning cloth should be white, clean, soft, non-linting cotton.

(3) Use the "double cloth wiping" method to clean the surface of the substrate. Soak a clean cloth with solvent. Wipe the surface of the substrate in only one direction. Before the solvent evaporates, immediately use a second cloth with a clean dry surface. Wipe the solvent off the surface of the substrate.

(4) Do not put the soaking rag into the container for soaking, otherwise the clean solvent will be contaminated and the cleaning effect will be affected.

(5) Only clean the bonding and sealing construction part within 1 hour each time. Do not expose the cleaned substrate surface to the air for too long.

2. Make a bet
Use plastic tape to cover the surface near the interface to ensure that the sealing working lines are perfectly neat.
Cut the mouth of the hose, install the pointed tube, and then cut it at a 45° angle according to the size of the gap.
Install the sealant gun and press out the sealant along the gap at a 45° angle to ensure that the sealant is in close contact with the surface of the base material. When the joint width is greater than 15 mm, sealant needs to be applied multiple times. After gluing, trim the surface with a knife to remove excess sealant, then tear off the tape. If there are stains, use a damp cloth to remove them.

3. Pad material
Open-cell polyurethane or closed-cell polyethylene foam padding rods and polyethylene materials are recommended lining materials. Prevent sealant from sticking on three sides.

 

STORAGE & SHELF LIFE
Store the original sealant in a dry place, the temperature should not be higher than 27 degrees, the storage period is 12 months from the date of production.
 

PACKAGE

Standard 300ml plastic plastic bottle packing, 24 pcs/ctn; 500ml flexible film packing, 20 pcs/ctn;200L iron drum.
Store the original sealant in a dry place, the temperature should not be higher than 27 degreesCelsius, from the date of production, the storage period of 12 months.

 

Company Profile

Nanjing Howell New Materials Technology Co., Ltd.
Room 501, Unit 7, Xingzhihui, Xinghuo Rd 19th, Jiangbei New District, Nanjing, (211899), Jiangsu, China.

American Warehouse:Add: 1006 CROCKER RD, DOOR E5, WESTLAKE, OH 44145