Two-component Thermally Conductive Flame-retardant Polyurethane Adhesive.

Product Description

Product Description

PU9208 is a two-component thermally conductive flame-retardant polyurethane adhesive. It is applied by mixing the two components in the proper ratio. It features high strength, excellent adhesion, impact resistance, good thermal conductivity, and flame-retardant properties. Additionally, it exhibits water resistance, electrical insulation, and corrosion resistance. PU9208 is widely used in bonding composite panels and assembling metal materials and fiber-reinforced composites.

Application

Suitable for structural bonding and fixation of composite materials such as SMC, FRP, CFRP, ABS, as well as bonding between composite materials and metal materials, or between metal materials.
Applicable for structural bonding between power battery cells, with excellent performance in PET film bonding, aluminum-plastic film bonding, PI film bonding, etc.

Features

Excellent thermal conductivity

Meets high flame retardancy requirements

Outstanding flexibility and impact resistance

Excellent resistance to aging and chemical media

Technical data

Before curing:

Appearance	A	Black
	B	Light yellow
Vis. (mPa·s)	A	60,000
	B	20,000
Mixing Ratio A:B (Volume Ratio)	1:1
Mixing Color	Black
Mixing Density	1.80
Operating Time (min)	6
Curing Time (min)	10

After curing:

Thermal conductivity (W/m·K):	1.5
Flame retardancy rating (UL-94):	V0
Shear strength (Al3003-Al3003, MPa):	6.0
Shear strength (PET blue film-PET blue film, MPa):	1.6
Tensile strength (MPa):	6.0
Elongation at break (%):	55
Hardness (Shore A):	90
Recommended operating temperature (ºC):	-40 to 100

Note: Testing and curing are under standard conditions of 23°C, 50%RH.

Usage Guidelines

The surface of the adhered materials should be cleaned in advance to ensure that it is clean, dry, oil-free, and dust-free.
When using two-component cartridge products, place the product in the matching caulking gun, gently push the plunger until both components are dispensed simultaneously, and then install the mixing nozzle.
Apply the adhesive evenly and continuously during application. The adhesive may gradually cure in the mixing nozzle if left unused for an extended period.
After applying the adhesive to assembled components, quickly close and press them together to ensure that the adhesive fully wets the substrate.
Temperature significantly affects the working time and curing of the adhesive. The operating temperature should not be below 10°C, with a recommended range of 15-25°C.
Heating can accelerate curing; choose appropriate conditions based on actual sample experiments.
Unused adhesive should be stored in a sealed state for future use. When resuming application, replace the mixing nozzle with a new one.

Storage and Shelf Life

Components A and B of the product are highly sensitive to moisture and therefore need to be stored in sealed packaging. If components A and B cannot be used up at once, please seal them tightly immediately after use to prevent moisture from entering and affecting the next use. It is recommended to store components A and B at temperatures between 15-30°C. During transportation, temperatures can drop to 0°C, but prolonged storage at this temperature is not advisable. If crystallization occurs, do not use the product.
Store in a cool, dry place, sealed, with a shelf life of at least 6 months at temperatures between 15-25°C.

Package

50mL; 400mL sausage; 20L

About Us

Nanjing Howell New Material Technology Co., Ltd.
Room 501, Unit 7, Xingzhihui, Xinghuo Rd 19th, Jiangbei New District, Nanjing, (211899), Jiangsu, China.

Acsic Ingredients, LLC.
Add: 565 Metro Place South STE 300 Dublin, OH 43017.

Factory:
No.1008, Panshan Village, Lipu Town, Zhuji City, Shaoxing City, Zhejiang Province, China.